Galvinoleum 3202 should be used on galvanised steel, stainless steel, aluminium, copper, glass, porcelain and other smooth, dense surfaces. Only intended for brush application. Can be recoated with Alkythane® 7500, improving the adhesion on very smooth and nonporous surfaces.
Remove grease, oil and all other surface contaminations by alkaline or high pressure (steam) cleaning in combination with appropriate detergents. Remove previous coatings completely. Remove salts, 'white rust', etc., by washing with Surfa-Etch 108 Etching Solution. The surface must be clean and dry during application.
Directions For Use
To ensure homogeneity, coating materials should be thoroughly stirred prior to use.
Temperature of air, substrate and coating material between 5 and 35°C and relative humidity below85%. The substrate temperature must be at least 3°C above dewpoint.
Application & Thinning: Brush
Use natural bristles, long hair brushes.
Application & Thinning: Roller
- Density (g/cm³): 0,92
- Gloss Level: Gloss
- Corrosion Class: C1/C2 low protection
- Solids content in volume: 20%
- Heat Resistance: 100 °C (dry heat)
Dry Times By 20º C/RV 50%
- Touch dry: Remains tacky
- Dry to handle: Remains tacky
- Dry to recoat: After 30 minutes but within 24 hours
- Fully cured: 24 hours
Recommended Wet Film Thickness
Recommended Dry Film Thickness
Practical coverage depends on many factors such as roughness of the substrate and material losses during application.
- VOC level: 745 g/l
- VOC readymix: 745 g/l
- VOC category: A/h
- VOC limit: 750 g/l
Remarks regarding safety: Consult Safety Data Sheet and Safety Information printed on the can.
- 1L & 5L
- Transparent Blue
- 50 m²/l
- For Use On
- Application Method
- Recoat Time (20°c)
- After 30 minutes but within 24 hours