Rustoleum Hard Hat® Aerosol Topcoats 2200 are based on a fast drying short oil soya alkyd. The products are based on lead and chromate free pigments.
Rustoleum Hard Hat® Aerosol Topcoats 2200 are based on a fast drying short oil soya alkyd. The products are based on lead - and chromate free pigments.
Features:
Recommended Use
RUST-OLEUM Fluorescent Topcoats 2200 should be applied over RUST-OLEUM Hard Hat 2190 Flat White; for exterior applications it is recommended to recoat Fluorescent Topcoats 2200 with RUST-OLEUM Hard Hat 2500 Clear. RUST-OLEUM Fluorescent Topcoats 2200 are intended for safety marking or signalling. RUST-OLEUM Fluorescent Topcoats 2200 should be used in light industrial exposures, normal humidity and interior applications.
Surface Preperation
Remove dirt, grease, oil and all other surface contaminants by appropriate means. Sand intact coatings to roughen the surface slightly. The surface must be clean and dry during application.
Application Conditions
For good results the relative humidity shall be below85% and the temperature of the can and substrate above 0°C.
Application & Thinning: Aerosol
Remove cover cap. Shake vigorously for at least one minute after the rattle of mixing ball is heard. Shake frequently during use. Hold can approx. 25 cm from surface. Use back and forth motion keeping can parallel with surface. Ensure that can is in motion when spray button is pressed to avoid runs and sags. Apply several thin layers at a few minutes interval to achieve adequate coating thickness. After use turn can upside down and press spray button for 2 - 3 seconds to clean valve.
Technical Data
Gloss Level: Matt Heat Resistance: 100°C (dry heat)
Dry Times By 20º C/RV 50%
Touch dry: 15 minutes
Dry to handle: 30 minutes
Dry to recoat: After 1 hour
Fully cured: 3 days
Recommended Wet Film Thickness
100 µm
Recommended Dry Film Thickness
25 µm
Theoretical Coverage
2.1 m² per spray can at 25 µm dry
Practical Consumption
Practical coverage depends on many factors such as porosity and roughness of the substrate and material losses during application.
Data sheet
Specific References